模具鋼H13
H13是一種熱作模具鋼工具鋼,即使處于高溫下也可以保持一定的強度,在注塑成型等過程中,傳統(tǒng)上常用于注塑成型和壓鑄等過程中的工具和模具制造
H13是一種應(yīng)用廣泛的高性能工具鋼,擁有優(yōu)良的紅硬性及耐熱疲勞性,高韌性、高延展性和良好的磨性。
H13工具鋼比17-4PH值的不銹鋼更硬,在高溫下能夠保持材料性能,是一種用途非常廣泛的材料Markforged H13可熱處理至45HRC,最高熱處理強度為1500
MPa,被Markforged客戶用于刀具、釬焊夾具和其他需要硬度或耐熱性的部件
MATERIAL DATASHEET
H13Tool Steel
Composition | Amount |
Chromium | 4.7-5.5% |
Molybdenum | 1.3-1.7% |
Silicon | 0.8-1.2% |
Vanadium | 0.8-1.2% |
Carbon | 0.3-0.45% |
Manganese | 0-2-0.5% |
Phosphorous | 0.03% max |
Sulfur | 0.03% max |
Iron | ba! |
? Markforged H13 As-Sintered
H13 Ibol Steel printed on the Metal X washed in the and sintered
in the Sinter-1. As Sintered Microstructure is pictured to the left
? Markforged H13 Heat Ideated
H13 Idol Steel printed Wi the Metal X system, air quenched at 1010C
and double tempered at 600C
? Wrought H13 Heat Treated
Wrought H13 too! steel standard from ASM Spedafty Handbook-air
quenched at 1010C and double tempered at 600C.
Typical Mechanical Properties | Standard | Markforged As-Sintered | Markforged Heat Treated | Wrought Heat Treated* |
Ultimate Tensile Strength | ASTME8 | 1420 MPa | 1500 MPa | 1580 MPa |
0Z2% Yield Strength | ASTME8 | 800 MPa | 1250 MPa | 1360 MPa |
Elongation at Break | ASTME8 | 5% | 5% | 14% |
Hardness | ASTME18 | 40HRC | 45HRC | 46HRC |
Relative Density | — | 2 94.5% | 2:94.5% | 100% |